Mullen burst tester TP-K11

Mullen burst tester TP-K11

Mullen burst tester TP-K11 is used to measure the bursting strength of paper submitted to increasing hydraulic pressure. Used in testing bursting strength of all types of papers in the 0 to 1600 kPa range depending on clamp pressure. It has mechanically & electrically integrated modern design, with compact structure & easy for maintenance. The advantage of user-friendly operations, stable performance makes this tester an essential instrument for papermaking, packing, inspection and research.

Measurement range 0 to 1600 kPa
Accuracy ± 0.5 % F.S.
Compression speed 95 ± 5 ml/min
Clamp pressure ≥ 430 kPa
Diameter of upper clamp 30.5 ± 0.05 mm
Diameter of lower clamp 33.1 ± 0.05 mm
Pneumatic pressure 0.3 to 0.5 MPa
Film resistance For bulge height = 9 mm, The pressure = 25 to 35 kPa
Dimension 480×420×600 mm
Net weight 65 kg
Power supply AC220 V ± 10 % , 50 Hz
  • Large colored LCD touch screen display
  • Bursting strength range 0 to 1600 kPa
  • Use of hydraulic oil as the driving force to break the specimen
  • Equipped with high precision sensors
  • Equipped micro-computer control system
  • Attachment for micro-printer with high print speed and low failure rate
  • Specimen is broken , stores the maximum amount automatically
Mullen burst tester is used to measure bursting strength of paperboard, paper across paper industry, packaging industry, printing industry.

Mullen burst tester TP-K11

Mullen burst tester TP-K11

Paper Testing Instruments
Whiteness and chromaticity tester TP-A10

Whiteness and chromaticity tester TP-A10
  • Sample (size) length
  • Diameter ≥30 mm, Thickness ≤ 40 mm
  • Measurement mode
  • Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b
  • Stability
  • ≤ 0.1 within 30 min
Coefficient of friction tester TP-D10

Coefficient of friction tester TP-D10
  • Measurement range
  • 0.01 to 10 N
  • Slider weight
  • 200 g
  • Slider size
  • 63×63 mm
Standard strip cutter TP-G10

Standard strip cutter TP-G10
  • Sample width
  • 15 mm
  • Sample maximum length
  • 300 mm
  • Parallelism
  • ≤ 0.1 mm
Internal Ply bond Tester TP-J11

Internal Ply bond Tester TP-J11
  • Capacity
  • A: 20 to 500 J/m2 B: 500 to 1000 J/m2
  • Impact angle
  • 90°
  • Unit
  • Lb-ft/in2  J/m2

Plastic Testing Instruments
Melt flow Indexer TMFI-A10

Melt flow Indexer TMFI-A10
  • Measuring range
  • 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density)
  • Measuring rate
  • 0.001 S
  • Temperature range
  • 50 to 400°C
Vacuum Leak Tester TVLT-A10

Vacuum Leak Tester TVLT-A10
  • Vacuum degree
  • 0 to 90 KPa
  • Accuracy
  • 1 % FS
  • Resolution
  • 0.1 KPa
Heat sealer THS-A10

Heat sealer THS-A10
  • Seal temperature
  • Room temperature -250°C
  • Control accuracy
  • ± 0.2°C
  • Dwell time
  • 0.1 S to 999.9 S
Primary adhesive tester TPAT-A10

Primary adhesive tester TPAT-A10
  • Inclined adjustable angle
  • 0 to 40°
  • Panel width
  • 120 mm
  • Test area width
  • 80 mm

Rubber Testing Instruments
DIN abrasion tester TDAT-A10

DIN abrasion tester TDAT-A10
  • Test arm weight
  • 2.5 N
  • Additional Loads
  • 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N,
  • Idler
  • 150 mm
Rubber Low Temperature Brittleness Tester TRBT-A11

Rubber Low Temperature Brittleness Tester TRBT-A11
  • Temperature control range
  • Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
  • Temperature accuracy
  • ± 0.3 ℃
  • Impact speed
  • 0℃ to -30℃ around 2.5 ℃/min '-30℃ to -40℃ around 2.5 ℃/min '-40℃ to -70℃ around 2.0 ℃/min
Rubber-weiss plasticity testing machine TRWM-A10

Rubber-weiss plasticity testing machine TRWM-A10
  • Temperature range
  • RT 50° to 300°
  • Temperature accuracy
  • ± 1°
  • Measuring range
  • 0.01 to 25 mm
Mooney viscometer TMV-A10

Mooney viscometer TMV-A10
  • Control temperature range
  • Normal temperature to 200°C
  • Temperature display resolution
  • 0.01°C
  • Temperature control accuracy
  • ± 0.3°

NDT Testing Instruments
Rockwell hardness meter TRHM-A11

Rockwell hardness meter TRHM-A11
  • Preliminary test force
  • 98 N
  • Total test force
  • 588, 980, 1471 N
  • Total test force dwell time
  • 1 to 30 S
Portable Vibration Calibrator LPVC-A10

Portable Vibration Calibrator LPVC-A10
  • Frequency (continually adjustable)
  • 10 Hz to1280 Hz + 0.01 %
  • Amplitude acceleration ( at 30m/s2 pk )
  • 40 Hz to 320 Hz + 0.3 dB + 1 digit
  • Amplitude velocity ( at 25mm / sec pk )
  • 40 Hz to 320 Hz + 0.5dB +1 digit
Digital Brinell hardness Tester TDBH-A10

Digital Brinell hardness Tester TDBH-A10
  • Test force
  • 612.5 N, 980 N, 1225 N
  • Brinell hardness test
  • 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
  • Hardness measuring area
  • 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter TRHM-A10

Rockwell hardness meter TRHM-A10
  • Preliminary test force
  • 98 N
  • Total test force
  • 588, 980, 1471 N
  • Total test force dwell time
  • 0 to 30 S

Other Testing Instruments
Benchtop gloss meter TBGM-A10

Benchtop gloss meter TBGM-A10
  • Test angle
  • 60°
  • Gloss aperture
  • 2 × 3 mm
  • Measurement range
  • 0 to 1000 GU